COATINGS

Texfire coatings are made paring from a flame retardant textile basis and a coating is applied to boost or increase functional and technical features. Coatings could be applied in one or both sides of the fabric. Texfire works with different types of coating, depending on their final application:

Through the fabric coating process, Texfire can customize and design the most suitable product for each situation. Possibility of different colours, different coating grammages, adjusting impermeability, resistance to wind penetration, resistance to melted metal impacts or its behaviour before extreme weldings.

Flire resistant fiberglass fabric with silicone coating on one side, designed to withstand splashes during welding.

Composition: 84%GL 16%SIL
Resistance: 250ºC in continuous. Punctual of 550ºC
Weight: 490 g/m² ±5%
Width: 150 cm
Featured: Resists molten metal splashes

Flame retardant fiberglass fabric with silicone coating on both sides, designed to withstand splashes during welding work. Admits its use vertically.

Composition: 72%GL 28%SIL
Resistance: 250ºC in continuous. Punctual of 900ºC
Weight: 590 g/m² ±5%
Width: 150 cm
Featured: Resists molten metal splashes

Fibreglass composite fabric for mechanical strength and flexibility, with a grey silicone coating for high temperatures on both sides.

Composition: 72% E-glass 28% Ht silicone
Resistance: 300 ºC in continuous. Punctual of 900ºC
Weight: 590 gr/m² ±5%
Width: 150 cm
Featured: Impermeable to liquids and fumes, and can be used on both sides.

High temperature fabric woven from steel-reinforced fiberglass.

Composition: 88% Eglass 10% HT AL PU 2% Stainless Steel
Resistance: 750ºC
Weight: 710 gr/m² ±5%
Width: 155 cm ±2%
Featured: Water and oil proof, welding protection.


Flame retardant fabric made of texturized fiberglass with a stainless steel filament armouring.

Composition: 94% E-glass 4% Stainless steel 2% Calcium silicate
Resistance: 700ºC in continuous
Weight: 1200 gr/m² ±50 gr/m²
Width: 150 cm
Featured: Excellent mechanical resistance and flame blocking.

Fabric composed by an E-glass type fiberglass base of 1000gsm, offers a great mechanical resistance and is coated with a chemical treatment of vermiculite.

Composition: 72% PTFE 28% GL
Resistance: 600ºC in continuous
Weight: 1035 g/m² ±5%
Width: 100 cm
Featured: Excellent thermal conductor, resistant to abrasion and welding impacts

Fabric of mineral origin with a chemical treatment of vermiculite to enhance its dimensional stability, its resistance against chemical agents, abrasion and tears.

Composition: 100% Sílica
Resistance: 950ºC in continuous
Weight: 650 g/m² ±5%
Width: 91 cm ±2%
Featured: Excellent thermal resistance

Flame retardant fabric for high temperatures based on silica fibers

Composition: Silica
Resistance: 1100 ºC in continuous. Punctual of 1500ºC
Weight: 630 gr/m² ±5%
Width: 92 cm ±2%
Featured: Resists high temperatures, slow cooling

Technical flame retardant fabric recovered of PTFE in both sides, is an excellent thermal conductor, as well as thermo-weldable. Non flammable, resistant to fire.

Composition: 58%PTFE 42%GL
Resistance: -50ºC a +260ºC
Weight: 250 g/m² ±5%
Width: 100 cm
Featured: Resists chemical agents, acids and solvents

Flame retardant fabric for high temperatures composed of a fiberglass core that incorporates a coating based on a polymer on both sides.

Composition: 93% Eglass 7% PU
Resistance: 550ºC in continuous
Weight: 460 gr/m² ±5%
Width: 200 cm ±2%
Featured: Excellent thermal resistance, electrical insulation.